S151 / S151D (Jethete M152 / MSRR 6503) , UNS S64152
Jethete M152 is a high-strength, creep and corrosion-resistant stainless steel, hardened and tempered for service up to 560°C. Its exceptional toughness and creep rupture strength make it ideal for highly stressed aerospace components, including turbine blades, discs, fasteners (bolts/screws), and rings.
| Standard | Grade | UNS | EN (EU) | Werkstoff Nr. |
|---|---|---|---|---|
| AMS | AMS 5719 | S64152 | - | - |
| MSRR | MSRR 6503 | - | - | - |
| DIN | 1.4939 | - | X12CrNiMo12 | 1.4939 |
| TLV | 1.4938 | - | X12CrNiMoV12-3 | 1.4938 |
| BS | BS S151 / S151D | - | - | - |
| French AFNOR | Z12CN12-02 | - | - | - |
Table of Contents
What is S151 / S151D (Jethete M152 / MSRR 6503) , UNS S64152?
S151 / S151D (Jethete M152 / MSRR 6503) Stainless Steel
BS S151 (Jethete M152) is a high-performance precipitation-hardening stainless steel designed for aerospace applications. It offers exceptional creep resistance, corrosion resistance, and mechanical strength at elevated temperatures (up to 560°C). Commonly used in turbine blades, discs, and fasteners.
Applications
- Turbine blades & discs
- High-stress bolts (AMS 5719)
- Aerospace fasteners (MSRR 6503)
- Exhaust systems (up to 560°C)
Chemical Composition (%)
| Element | Min (%) | Max (%) | Typical (%) |
|---|---|---|---|
| C | - | 0.12 | 0.08 |
| Cr | 11.0 | 13.0 | 12.0 |
| Ni | 2.0 | 3.0 | 2.5 |
| Mo | 1.0 | 2.0 | 1.5 |
| Mn | - | 1.0 | 0.5 |
| Si | - | 1.0 | 0.3 |
| P | - | 0.04 | 0.02 |
| S | - | 0.03 | 0.01 |
| Fe | Balance | ~82.0 |
Material Properties
Room Temperature Properties (Tempered Condition - BS S151D)
| Property | Value (Typical) | Test Standard |
|---|---|---|
| Tensile Strength (UTS) | 850-1000 MPa | ASTM E8 |
| Yield Strength (0.2%) | 700-850 MPa | ASTM E8 |
| Elongation (% in 50mm) | 15-20% | ASTM E8 |
| Hardness (HRC) | 28-35 | ASTM E18 |
| Impact Toughness (Charpy) | 50-70 J | ASTM E23 |
Elevated Temperature Properties
| Temperature (°C) | Creep Rupture Strength (1000h, MPa) | Oxidation Resistance |
|---|---|---|
| 500 | 300 | Excellent |
| 560 | 200 | Good |
| 600 | 120 | Limited |
Physical Properties
| Property | Value |
|---|---|
| Density (g/cm³) | 7.8 |
| Melting Range (°C) | 1400-1450 |
| Thermal Conductivity (W/m·K @ 20°C) | 15.0 |
| Electrical Resistivity (Ω·m) | 0.75 × 10⁻⁶ |
| Magnetic Permeability | Austenitic (Non-magnetic) |
Heat Treatment
- Softening (BS S151A): 670-720°C × 6h, air cool
- Hardening: 1050°C ±10°C, air cool
- Tempering (BS S151D): 650°C ±5°C, air cool
Processing Performance
- Machinability: 60% of AISI 304 (use carbide tools, low speeds)
- Welding: TIG/MIG possible with matching filler (post-weld heat treatment required)
- Forging: 1050-900°C (avoid <850°C to prevent cracking)